Elastomer-based compound can be moisture cured with the addition of a catalyst masterbatch (Sioplas method). It is a cable compound for insulation and jacketing.
Cable insulation with a proper mixture of KKX-420G (95 parts) and CAT-XL (5 parts) ex hibits excellent thermo- oxidative stability.
Product Information:
KKX-423/CAT-XL silane crosslinkable natural compound system designed for insulation of low voltage energy cables. KKX-423 / CAT-XL is designed for Insulation of low voltage energy cables, range up to 6 kV.
KKX-423 is a low density polyethylene, copolymerised with vinyl silane. CAT-XL is an ambient crosslinking catalyst masterbatch specially designed to be used. The system is highly active and crosslinks quickly at in sauna or in hot water.
The proper mixture could be;
• 95% for KKX-423 (base polymer), 5% for CAT-XL (catalyst)
Crosslinking by immersion in 90°C hot water 2-6 hours; by exposure to low pressure water steam, 12-15 hours. It cures after 72 hours at room conditions.
Product Information:
KKX-MXLPE/CAT-XL is a silane crosslinkable medium density polyethylene natural compound system designed for insulation of low voltage energy cables.
KKX-MXLPE is a medium density polyethylene, copolymerised with vinyl silane. CAT-XL is an ambient crosslinking catalyst masterbatch specially designed to be used. The system is highly active and crosslinks quickly at in sauna or in hot water.
Cable insulation with a proper mixture of KKX-MXLPE (95 parts) and CAT-XL (5 parts) exhibits excellent thermo-oxidative stability. The combination is suitable for both copper and aluminum conductors.
Crosslinking by immersion in 90°C hot water 2-6 hours; by exposure to low pressure water steam, 12-15 hours. It cures after 72 hours at room conditions.
Product Information:
KKX-XLPE1/CAT-XL is a silane crosslinkable natural compound system designed for insulation of low voltage energy cables. KKX-XLPE1 / CAT-XL is designed for Insulation of low voltage energy cables, range up to 6 kV.
KKX-XLPE1 is a low density polyethylene, copolymerised with vinyl silane. CAT-XL is an ambient crosslinking catalyst masterbatch specially designed to be used. The system is highly active and crosslinks quickly at in sauna or in hot water.
The combination is suitable for both copper and aluminum conductors. If the insulation is designed to meet the thermo-oxidative ageing demand required by IEC 60502 at 150°C in contact with copper, the addition of 9 parts KKX-XLPE1 to CAT-XL is recommended.
The proper mixture could be;
• 95% for KKX-XLPE1 (base polymer), 5% for CAT-XL (catalyst)
• 93% for KKX-XLPE1 (base polymer), 7% for CAT-XLB (black catalyst)
Crosslinking by immersion in 90°C hot water 2-6 hours; by exposure to low pressure water steam, 12-15 hours.